Radio-frequency (RF) hydrogen plasma treatment, thermal annealing in a furnace, and rapid thermal annealing of high-dose P+ ion implanted p-type Ge layers have been studied by Raman scattering spectroscopy, atomic force microscopy, secondary ion mass spectrometry, electrochemical capacitance–voltage profiling, four-point probes method, and x-ray reflectometry. It was shown that low-temperature RF plasma treatment at temperature about 200 °C resulted in full recrystallization of amorphous Ge layer implanted by P+ ions and activation of implanted impurity up to 6.5 × 1019 cm−3 with a maximum concentration at the depth of about 20 nm. Rapid thermal annealing (15 s) and thermal annealing (10 min) in nitrogen ambient required considerably higher temperatures for the recrystallization and activation processes that resulted in diffusion of implanted impurity inside the Ge bulk. It was demonstrated …
American Vacuum Society
Publication date: 
1 Sep 2017

Alexei N Nazarov, Volodymyr O Yukhymchuk, Yurii V Gomeniuk, Sergiy B Kryvyi, Pavel N Okholin, Petro M Lytvyn, Vasyl P Kladko, Volodymyr S Lysenko, Volodymyr I Glotov, Illya E Golentus, Enrico Napolitani, Ray Duffy

Biblio References: 
Volume: 35 Issue: 5 Pages: 051203
Journal of Vacuum Science & Technology B, Nanotechnology and Microelectronics: Materials, Processing, Measurement, and Phenomena